Creating crystalline silicon core fibers from aluminum and glass preforms

Figures: a, schematic of aluminum-core-quartz-cladding preform drawn into Silicon-core fiber. b, the chemical reaction at the core-cladding interface. Al atoms (blue) break Si-O bonds, reduce Si (black), release O2- ions (red), and change to Al3+ ions (green). All the products of ions and atoms dissolve in the Al melt and diffuse into the core. c, the Si atoms (black), because of their miscibility, diffuse and remain in the Al melt (blue), while ions of O and Al form Al2O3 molecules (yellow) and precipitate out at the bottom. d-g, the SEM and EDX analysis on cross section of the Si-core fiber. Scale bar: 100 µm in d, 50 µm in e-g.

Crystalline silicon is a critically important electronic material in all consumer electronic products. The ability to create fibers from this material would open up exciting vistas for a new generation of fiber-based electronic and optical devices. Traditional fiber-optic drawing involves a thermally mediated geometric scaling where both the fiber materials and their relative positions are identical to those found in the fiber preform. To date, all thermally drawn fibers are limited to the preform composition and geometry.

MIT MRSEC researchers have demonstrated (see figure) that it is possible to fabricate a meter-long crystalline silicon-core, silica-cladded fiber from a preform that does not contain any elemental silicon but rather aluminum and silica (glass). The ability to produce crystalline silicon core fibers out of inexpensive aluminum and glass paves the way for a simple and scalable method of incorporating silicon-based electronics and and photonics into fibers.

 

Hou, C., Jia, X., Wei, L., Tan, S-C., Zhao, X., Joannopoulos, J.D., Fink, Y., Crystalline Silicon Core Fibres from Aluminium Core Preforms, Nature Communications 6, number:6248, DOI:doi:10.1038/ncomms7248, February 2015.

This work was supported in part by the MIT MRSEC through the MRSEC Program of the National Science Foundation under award number DMR-1419807.

 

Highlights Main Index

CMSE Home

Research

Educational Outreach

Facilities

Connecting to Industry

Highlights

News and Publications

People

About CMSE

Related Links

BUILDING INFO & SAFETY | CONTACT US | SEARCH | MATERIALS CALENDAR
CMSE Nuggets