Using Nanotubes in Computer Chips
A new technique for growing carbon nanotubes should be easier to integrate with existing semiconductor manufacturing processes
Results: Researchers in the lab of MIT materials science professor Carl V. Thompson grew dense forests of crystalline carbon nanotubes on a metal surface at temperatures close to those characteristic of computer chip manufacturing. Unlike previous attempts to do the same thing, the researchers' technique relies entirely on processes already common in the semiconductor industry. The researchers also showed that the crucial step in their procedure was to preheat the hydrocarbon gas from which the nanotubes form, before exposing the metal surface to it.
Why it matters: The transistors in computer chips are traditionally connected by tiny copper wires. But as chip circuitry shrinks and the wires become thinner, their conductivity suffers and they become more likely to fail. A simple enough manufacturing process could enable carbon nanotubes to replace the vertical wires in chips, permitting denser packing of circuits.
How they did it: In a vacuum chamber, the researchers vaporized the metals tantalum and iron, which settled in layers on a silicon wafer. Then they placed the coated wafer at one end of a quartz tube, which was inserted into a furnace. At the wafer's end of the tube, the furnace temperature was 475 degrees C; but at the opposite end, the temperature varied. The researchers pumped ethylene gas into the tube from the end opposite the wafer. When the temperature at that end approached 800 degrees, the ethylene decomposed, and the iron on the wafer catalyzed the formation of carbon nanotubes.
Next steps: The researchers are trying to determine whether different combinations of metals and hydrocarbon gases can lower the catalytic temperature even further and improve the quality of the nanotubes.
Funding: The research was sponsored by the MARCO Interconnect Focus Center and partially by Intel (Gilbert Nessim, who was a graduate student in Thompson's lab, was supported by an Intel Fellowship).