Mi 01.11.2000 at 03:41:27 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.80 nm Difference : 0.05° Phi: 65 70 Psi: 43.29 42.67 Delta: 97.29 79.00 ------------------------------------------------------- Mi 01.11.2000 at 03:41:33 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.80 nm Difference : 0.05° Phi: 65 70 Psi: 43.29 42.67 Delta: 97.29 79.00 ------------------------------------------------------- Mi 01.11.2000 at 03:41:48 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.80 nm Difference : 0.00° Phi: 65 70 Psi: 43.30 42.65 Delta: 97.34 79.03 ------------------------------------------------------- Mi 01.11.2000 at 03:42:07 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.79 nm Difference : 0.04° Phi: 65 70 Psi: 43.29 42.65 Delta: 97.29 79.03 ------------------------------------------------------- Mi 01.11.2000 at 03:42:12 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.79 nm Difference : 0.04° Phi: 65 70 Psi: 43.29 42.65 Delta: 97.29 79.03 ------------------------------------------------------- Mi 01.11.2000 at 03:42:36 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.79 nm Difference : 0.04° Phi: 65 70 Psi: 43.29 42.65 Delta: 97.29 79.03 ------------------------------------------------------- Mi 01.11.2000 at 03:42:39 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.79 nm Difference : 0.04° Phi: 65 70 Psi: 43.29 42.65 Delta: 97.29 79.03 ------------------------------------------------------- Mi 01.11.2000 at 03:42:50 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.79 nm Difference : 0.04° Phi: 65 70 Psi: 43.29 42.65 Delta: 97.29 79.03 ------------------------------------------------------- Mi 01.11.2000 at 04:58:51 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.78 nm Difference : 0.05° Phi: 60 65 70 Psi: 44.19 43.29 42.66 Delta: 114.16 97.31 78.97 ------------------------------------------------------- Mi 01.11.2000 at 04:59:38 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.78 nm Difference : 0.05° Phi: 60 65 70 Psi: 44.19 43.29 42.66 Delta: 114.16 97.31 78.97 ------------------------------------------------------- Mo 19.02.2001 at 16:04:38 >Thickness and refr. index (multiple angle) Refractive index: 1.4670 Absol. thickness: 101.78 nm Difference : 0.05° Phi: 60 65 70 Psi: 44.19 43.29 42.66 Delta: 114.16 97.31 78.97 ------------------------------------------------------- So 18.03.2001 at 12:43:37 >Thickness and refr. index (multiple angle) Refractive index: 1.3130 Absol. thickness: 4.14 nm Difference : 0.18° Phi: 45 50 55 60 65 70 Psi: 34.37 31.37 27.71 23.20 17.64 10.53 Delta: 178.68 178.13 177.43 176.32 174.45 169.56 ------------------------------------------------------- So 18.03.2001 at 12:58:30 >Thickness and refr. index (multiple angle) Refractive index: 1.4280 Absol. thickness: 1.96 nm Difference : 0.20° Phi: 45 50 55 60 65 70 Psi: 34.39 31.38 27.69 23.21 17.59 10.43 Delta: 179.34 179.01 178.56 177.90 176.70 173.76 ------------------------------------------------------- So 18.03.2001 at 15:49:32 >Thickness and refr. index (multiple angle) Piece 1, immediately after plasma cleaning (also previous soak in H2SO4 for 2.5 hours, then rinse with water then methanol) Refractive index: 1.4650 Absol. thickness: 102.74 nm Difference : 0.01° Phi: 65 70 Psi: 43.78 43.09 Delta: 97.67 79.26 ------------------------------------------------------- So 18.03.2001 at 16:39:35 >Thickness and refr. index (multiple angle) Piece 1, after coating with amine silane Phi: 45 50 55 60 65 70 Psi: 34.38 31.36 27.73 25.10 17.98 11.65 Delta: 174.84 173.03 170.50 169.54 159.72 144.20 ------------------------------------------------------- So 18.03.2001 at 16:47:08 >Thickness and refr. index (multiple angle) Piece 1, after coating with amine silane Refractive index: 3.0850 Absol. thickness: 8.64 nm Difference : 1.56° Phi: 45 50 55 60 65 70 Psi: 34.38 31.36 27.73 25.10 17.98 11.65 Delta: 174.84 173.03 170.50 169.54 159.72 144.20 ------------------------------------------------------- So 18.03.2001 at 17:32:47 >Thickness and refr. index (multiple angle) Piece 1, after coating with amine silane Refractive index: 3.0760 Absol. thickness: 14.67 nm Difference : 7.05° Phi: 45 50 55 60 65 70 Psi: 34.38 31.36 27.73 25.10 17.98 12.58 Delta: 174.84 173.03 170.50 169.54 159.72 125.46 ------------------------------------------------------- So 18.03.2001 at 17:33:04 >Thickness and refr. index (multiple angle) Piece 1, after coating with amine silane Refractive index: 3.0660 Absol. thickness: 14.96 nm Difference : 8.17° Phi: 55 60 65 70 Psi: 27.73 25.10 17.98 12.58 Delta: 170.50 169.54 159.72 125.46 ------------------------------------------------------- So 18.03.2001 at 17:33:18 >Thickness and refr. index (multiple angle) Piece 1, after coating with amine silane Refractive index: 3.0560 Absol. thickness: 227.16 nm Difference : 1.69° Phi: 45 50 55 60 Psi: 34.38 31.36 27.73 25.10 Delta: 174.84 173.03 170.50 169.54 ------------------------------------------------------- So 18.03.2001 at 17:33:30 >Thickness and refr. index (multiple angle) Piece 1, after coating with amine silane Refractive index: 3.0460 Absol. thickness: 12.95 nm Difference : 2.01° Phi: 45 50 55 60 65 Psi: 34.38 31.36 27.73 25.10 17.98 Delta: 174.84 173.03 170.50 169.54 159.72 ------------------------------------------------------- So 18.03.2001 at 17:33:38 >Thickness and refr. index (multiple angle) Piece 1, after coating with amine silane Refractive index: 3.0310 Absol. thickness: 14.19 nm Difference : 7.05° Phi: 45 50 55 60 65 70 Psi: 34.38 31.36 27.73 25.10 17.98 12.58 Delta: 174.84 173.03 170.50 169.54 159.72 125.46 ------------------------------------------------------- So 18.03.2001 at 17:35:10 >Thickness and refr. index (multiple angle) Piece 1, after coating with amine silane Refractive index: 3.0470 Absol. thickness: 241.01 nm Difference : 25.47° Phi: 45 50 55 60 65 70 Psi: 34.39 31.40 27.71 23.24 20.43 12.58 Delta: 172.40 169.59 165.48 159.40 88.08 125.46 ------------------------------------------------------- So 18.03.2001 at 17:35:50 >Thickness and refr. index (multiple angle) Piece 1, after coating with amine silane Refractive index: 3.0370 Absol. thickness: 21.36 nm Difference : 3.32° Phi: 45 50 55 60 65 70 Psi: 34.39 31.40 27.71 23.24 18.04 12.58 Delta: 172.40 169.59 165.48 159.40 148.48 125.46 ------------------------------------------------------- Di 17.06.2003 at 17:54:53 >Thickness (fixed refr. index, mult. angle) Piece 1, after coating with amine silane Thickness: 71.99 nm Difference : 10.82° Phi: 60 65 70 Psi: 29.96 25.00 22.33 Delta: 121.85 96.05 69.10 ------------------------------------------------------- Di 16.12.2003 at 12:26:06 >Thickness (fixed refr. index, mult. angle) Piece 1, after coating with amine silane Phi: 70 Psi: 42.86 Delta: 79.10 ------------------------------------------------------- Di 16.12.2003 at 12:26:13 >Thickness (fixed refr. index, single angle) Piece 1, after coating with amine silane Angle Thickness Dev. 70 100.75 0.58 Phi: 70 Psi: 42.86 Delta: 79.10 ------------------------------------------------------- Di 16.12.2003 at 12:26:20 >Thickness (fixed refr. index, single angle) Piece 1, after coating with amine silane Angle Thickness Dev. 60 65.17 0.23 65 74.21 8.34 70 100.75 0.58 Phi: 60 65 70 Psi: 29.96 25.00 42.86 Delta: 121.85 96.05 79.10 -------------------------------------------------------